The difference in the progress of crystallization at different points in the casting material causes fast and abrupt growth of crystals.(a) True(b) FalseThe question was posed to me by my school principal while I was bunking the class.I want to ask this question from Mechanism of Solidification in chapter Cooling and Solidification of Casting-Forming-Welding I

The difference in the progress of crystallization at different points

1.	The difference in the progress of crystallization at different points in the casting material causes fast and abrupt growth of crystals.(a) True(b) FalseThe question was posed to me by my school principal while I was bunking the class.I want to ask this question from Mechanism of Solidification in chapter Cooling and Solidification of Casting-Forming-Welding I
Answer» Right answer is (b) False The explanation: The difference in the PROGRESS of crystallization at the different points in the CASTING material does not make fast growth of crystals, even this makes the hampering of CRYSTAL growth which basically restricts or retards the columnar growth of crystals starting from the MOULDING surface during casting process.

Discussion

No Comment Found

Related InterviewSolutions

Cold cracking failure of the casting product can be avoided by shot peening method which induces internal stresses in the casting.(a) True(b) FalseThis question was posed to me during a job interview.Question is taken from Residual Stress in chapter Cooling and Solidification of Casting-Forming-Welding I
Residual stresses can cause any defects in the casting except distortion of the casting component.(a) True(b) FalseThis question was addressed to me during an interview.I would like to ask this question from Residual Stress in chapter Cooling and Solidification of Casting-Forming-Welding I
Residual stresses can also be calculated the same way as the stresses due to the external loads is calculated.(a) True(b) FalseI got this question during an interview.This is a very interesting question from Residual Stress topic in chapter Cooling and Solidification of Casting-Forming-Welding I
Natural aging treatment is a fast and accurate method for reducing residual stresses in the casting compared to the heat treatment.(a) True(b) FalseThe question was asked during an interview for a job.I would like to ask this question from Residual Stress in division Cooling and Solidification of Casting-Forming-Welding I
In casting system, the riser is generally placed at the heaviest section to avoid defects from the casting.(a) True(b) FalseThe question was posed to me during an interview for a job.I need to ask this question from Riser Placement topic in chapter Cooling and Solidification of Casting-Forming-Welding I
By using resin bonded sand in the making of mould, the stresses produced in the casting can be reduced.(a) True(b) FalseI got this question in quiz.My question is taken from Residual Stress in division Cooling and Solidification of Casting-Forming-Welding I
Manufacturing process is the only consideration which can cause residual stresses in the casting.(a) True(b) FalseI got this question in an international level competition.This intriguing question comes from Residual Stress in division Cooling and Solidification of Casting-Forming-Welding I
It is always desirable to have a large volume of molten metal in the riser to make casting products.(a) True(b) FalseI had been asked this question during an interview.This question is from Riser Placement topic in portion Cooling and Solidification of Casting-Forming-Welding I
Minimization of friction between the mould and casting surface can reduce the chances of tearing of thin parts of the casting.(a) True(b) FalseThe question was posed to me during an interview for a job.My question is taken from Solidification with Predominant Resistance in Mould topic in chapter Cooling and Solidification of Casting-Forming-Welding I
Machinability of the casting product can be improved by reducing the residual stresses in the casting.(a) True(b) FalseThe question was posed to me during an interview.The doubt is from Residual Stress in portion Cooling and Solidification of Casting-Forming-Welding I

Discussion

No Comment Found

Related InterviewSolutions

Reply to Comment